Epoxy

EpoxAmite™ WHITE 102

EpoxAmite™ WHITE 102 is listed by Smooth-On as an epoxy resin system. The source reports mixed viscosity of 2,800 cps, mix ratio by weight of 100A:23B, pot life of 62 minutes. This record connects 19 reported fields with 3 manufacturer document links. Review the original technical data sheet for the applicable test conditions and processing instructions.

Technical data sheet Safety data sheet
2,800 cpsManufacturer-reported
100A:23BManufacturer-reported
62 minutesManufacturer-reported
24 hoursManufacturer-reported
85Manufacturer-reported
1.23 g/ccManufacturer-reported

Technical & safety documents

3 links
Files open on the manufacturer's document host. Region and language follow the source listing; confirm the revision inside the file.
Open original PDF
TDS
Technical BulletinEnglish · Not specified
Open file
SDS
EpoxAmite WHITE (Part A) SDS | EnglishEnglish · United States & Canada
Open file
SDS
102 Hardener (Part B) SDS | EnglishEnglish · United States & Canada
Open file

Reported specifications

19 fields
Material and processing data
PropertyReported valueEvidence
Mixed Viscosity2,800 cpsManufacturer table
ColorWhiteManufacturer table
Mix Ratio By Weight100A:23BManufacturer table
Pot Life62 minutesManufacturer table
Thin Film Working Time120 minutesManufacturer table
Cure Time24 hoursManufacturer table
Shore D Hardness85Manufacturer table
Specific Gravity1.23 g/ccManufacturer table
Specific Volume22.5 cu. in./lb.Manufacturer table
Compressive Strength11,960 psiManufacturer table
Flexural Modulus446,000 psiManufacturer table
Flexural Strength8,350 psiManufacturer table
Flexural Strength on 6 ply / 10 oz. Laminate31,600 psiManufacturer table
Heat Deflection Temp133 °FManufacturer table
Tensile Modulus557,000 psiManufacturer table
Ultimate Tensile5,600 psiManufacturer table
Ultimate Tensile on 6 ply / 10 oz. Laminate30,700 psiManufacturer table
Tensile Elongation1.2 %Manufacturer table
Compressive Modulus114,000 psiManufacturer table
Reported values are not independent test results. Original units and table wording are preserved. Extracted TDS rows can depend on the grade, component and source table headings; use the linked page to verify that context. Test methods, sample preparation and cure schedules may differ; consult the original TDS before making a performance comparison.

Selection & processing checks

Compare the complete resin–hardener system. A different hardener or cure schedule can change the cured properties.

  • Is the stated ratio by weight or by volume?
  • Do the thermal and mechanical values use the same cure schedule?
  • Is the formulation designed for casting, bonding or encapsulation?
  • Confirm the complete product designation, including any hardener, color or formulation suffix.
  • Read the current SDS for handling, protective equipment, storage and disposal information.

The reported weight ratio for this record is 100A:23B. A weight ratio must not be used as a volume ratio without the appropriate density information.

Missing properties are not estimated. Similar values or shared application labels do not establish a drop-in replacement.

Other materials in this family

View collection
Material / manufacturerFamilyKey specificationDocumentsAdd to comparison
EPO-TEK® 343ND-LHEpoxy TechnologyEpoxy2,580 cPsViscosity (23°C) @ 100 rpm3 linked
EPO-TEK® B9101-2 UnfilledEpoxy TechnologyEpoxy1,000 - 1,300 cPsViscosity (23°C) @ 100 rpm2 linked
EPO-TEK® B9126-8Epoxy TechnologyEpoxy11,000-18,500 | cPsViscosity (23°C) @ 20 rpm2 linked
EPO-TEK® E2101Epoxy TechnologyEpoxy15,000-18,000 cPsViscosity (23°C) @ 20 rpm3 linked
Related records are browsing suggestions, not validated substitutes.