Smooth-On / Material reference
EpoxyEpoxAmite™ HT
EpoxAmite™ HT is listed by Smooth-On as an epoxy resin system. The source reports mixed viscosity of 650 cps, mix ratio by weight of 100A:33B, pot life of 60 minutes. This record connects 21 reported fields with 2 manufacturer document links. Review the original technical data sheet for the applicable test conditions and processing instructions.
650 cpsManufacturer-reported
100A:33BManufacturer-reported
60 minutesManufacturer-reported
24 hoursManufacturer-reported
80Manufacturer-reported
1.10 g/ccManufacturer-reported
Technical & safety documents
2 linksFiles open on the manufacturer's document host. Region and language follow the source listing; confirm the revision inside the file.
Technical BulletinEnglish · Not specified
Open file EpoxAmite HT SDS | EnglishEnglish · United States & Canada
Open file Reported specifications
21 fieldsMaterial and processing data
| Property | Reported value | Evidence |
|---|---|---|
| Mixed Viscosity | 650 cps | Manufacturer table |
| Color | Clear | Manufacturer table |
| Mix Ratio By Weight | 100A:33B | Manufacturer table |
| Pot Life | 60 minutes | Manufacturer table |
| Thin Film Working Time | 180 minutes | Manufacturer table |
| Cure Time | 24 hours | Manufacturer table |
| Shore D Hardness | 80 | Manufacturer table |
| Specific Gravity | 1.10 g/cc | Manufacturer table |
| Specific Volume | 25.2 cu. in./lb. | Manufacturer table |
| Compressive Strength | 16,600 psi | Manufacturer table |
| Flexural Modulus | 429,000 psi | Manufacturer table |
| Flexural Modulus on 6 ply / 10 oz. Laminate | 2,216,000 psi | Manufacturer table |
| Flexural Strength | 12,325 psi | Manufacturer table |
| Flexural Strength on 6 ply / 10 oz. Laminate | 20,700 psi | Manufacturer table |
| Heat Deflection With Post Cure | 300 °F | Manufacturer table |
| Tensile Modulus | 342,000 psi | Manufacturer table |
| Tensile Modulus on 6 ply / 10 oz. Laminate | 2,150,000 psi | Manufacturer table |
| Ultimate Tensile | 6,500 psi | Manufacturer table |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 32,100 psi | Manufacturer table |
| Tensile Elongation | 2.3 % | Manufacturer table |
| Compressive Modulus | 168,000 psi | Manufacturer table |
Reported values are not independent test results. Original units and table wording are preserved. Extracted TDS rows can depend on the grade, component and source table headings; use the linked page to verify that context. Test methods, sample preparation and cure schedules may differ; consult the original TDS before making a performance comparison.
Selection & processing checks
Compare the complete resin–hardener system. A different hardener or cure schedule can change the cured properties.
- Is the stated ratio by weight or by volume?
- Do the thermal and mechanical values use the same cure schedule?
- Is the formulation designed for casting, bonding or encapsulation?
- Confirm the complete product designation, including any hardener, color or formulation suffix.
- Read the current SDS for handling, protective equipment, storage and disposal information.
The reported weight ratio for this record is 100A:33B. A weight ratio must not be used as a volume ratio without the appropriate density information.
Missing properties are not estimated. Similar values or shared application labels do not establish a drop-in replacement.
Other materials in this family
View collection| Material / manufacturer | Family | Key specification | Documents | Add to comparison |
|---|---|---|---|---|
| EPO-TEK® 301-1 | Epoxy | 80 - 100 cPs | 2 linked | |
| EPO-TEK® 320NC | Epoxy | 1,000 - 3,000 cPs | 2 linked | |
| EPO-TEK® 320NC-2 | Epoxy | 1,500 – 3,000 cPs | 2 linked | |
| EPO-TEK® 730 Black | Epoxy | 80,000-120,000 | cPs | 2 linked |